Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1001R TORAY JAPAN
Amilan®
--
Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 81 M（Scale） | |
| ISO 2039-2 | 119 R |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| dielectric constant | 23°C | IEC 60250 | 4.5 1kHz |
| Dissipation Factor | 23°C | IEC 60250 | 0.03 1kHz |
| dielectric constant | 23°C | IEC 60250 | 3.8 1MHz |
| Dissipation Factor | 23°C | IEC 60250 | 0.02 1MHz |
| dielectric strength | 3.00mm | IEC 60243-1 | 21 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 Ω.cm | |
| IEC 60093 | 1E+15 Ω.cm |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| bending strength | -40°C | ISO 178 | 160 Mpa |
| 23°C | ISO 178 | 145 Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Flexural modulus | -40°C | ISO 178 | 6900 Mpa |
| tensile strength | -40°C | ISO 527-2 | 130 Mpa |
| Flexural modulus | 23°C | ISO 178 | 5800 Mpa |
| elongation at break | -40°C | ISO 527-2 | 2.0 % |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 35 kJ/m² |
| elongation at break | 23°C | ISO 527-2 | 2.5 % |
| Rockwell hardness | ASTM D785 | R119.M81 | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 95 Mpa |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.51 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.9 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 0.75mm | |
| UL -94 | HB 1.50mm | ||
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.90 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1001R |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 173 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 203 °C |
| melting temperature | 225 ℃（℉） |