Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV30F 000000 ENVALIOR WUXI
Durethan®
Automotive connectors、Automotive components、Instrument accessories、Electronic and Electrical、Communication equipment
Heat aging
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Supplementary Information | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GFHR.14-110.GF30;ISO1043-PAGFFR(30+40+72) |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 23°C | ISO 178/A | 9800 Mpa |
| bending strength | 3.5%Strain | ISO 178/A | -- Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 150 Mpa |
| bending strength | 23°C | ISO 178 | 210 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 10800 Mpa |
| bending strength | FlexuralStrainatFlexuralStrength5(23°C) | 2.7 % |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 37 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| 0.8mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| 1.5mm | IEC 60695-2-13 | 775 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 775 °C |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.18 % |
| TD:280°C,2.00mm2 | ISO 294-4 | 0.62 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.5 % |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 23.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.0 % |
| Shrinkage rate | MD:280°C,2.00mm2 | ISO 294-4 | 0.22 % |
| MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.080 % |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/BKV30F 000000 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 224 °C | |
| vicat | ISO 306/B120 | 210 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 2.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 218 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8.1E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 204 °C |