POM GH-25XAP JAPAN POLYPLASTIC
DURACON®
Fitness equipment、Automotive Applications
wear resistant、High temperature resistan、Filler: Glass fiber reinf、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
Rockwell hardnessM级ISO 2039-295
Supplementary InformationTest ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
ColorNumberCF3500/CD3501
Electrical performanceTest ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
Volume resistivityIEC 600935E+13 ohms·cm
dielectric strength3.00mmIEC 60243-124 KV/mm
Surface ResistivityIEC 600934E+16 ohms
Mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
Wear factor0.060MPa,0.15m/sec7JISK721810000 10^-8mm³/N·m
Tensile modulusISO 527-28500 Mpa
coefficient of friction与钢-动态3JISK72180.60
bending strengthISO 178196 Mpa
Wear factor0.49MPa,0.30m/sec5JISK7218400 10^-8mm³/N·m
Tensile strain断裂ISO 527-22.4 %
Flexural modulusISO 1787900 Mpa
coefficient of frictionDynamic2JISK72180.37
Wear factor0.49MPa,0.30m/sec6JISK72187000 10^-8mm³/N·m
tensile strength ISO 527-2136 Mpa
Wear factor0.060MPa,0.15m/sec4JISK7218300 10^-8mm³/N·m
flammabilityTest ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
UL flame retardant ratingUL 94HB
physical property Test ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
Melt volume flow rate190°C/2.16kgISO 11339.00 cm3/10min
Water absorption rate23°C,24hrISO 620.60 %
melt mass-flow rate190°C/2.16kgISO 113312 g/10min
Thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/GH-25XAP
Linear coefficient of thermal expansionTD：23to55°C内部方法9E-05 cm/cm/°C
MD：23到55°C内部方法3E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A162 °C