PP J106G PRIME POLYMER JAPAN
PRIME POLYPRO
Industrial components、Household goods
High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| Melting Temperature | 15 ℃（℉） | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 100 °C |
| 0.45MPa | ISO 75 | 100 °C | |
| ASTM D648/ISO 75 | 100 ℃（℉） |
| Hardness | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| Rockwell Hardness | R计秤 | ISO2039-2 | 100 |
| Physical | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| Melt index | 230℃ | ISO 1133 | 15 g/10min |
| Density | ISO 1183 | 0.910 g/cm³ | |
| Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 15 g/10min |
| Mechanical Properties | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | 100 R scale | |
| Impact Strength | 23℃ | ISO 179 | 3.3 kJ/m² |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 100 % | |
| Rockwell Hardness | ASTM D785 | 100 | |
| Tensile Strength | ASTM D638/ISO 527 | 35.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile Stress | 屈服 | ISO527-2 | 35.0 Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 100 % |
| Tensile Elongation | 断裂 | ISO 527 | 100 % |
| Tensile Strength | ISO 527 | 35.0 Mpa | |
| Flexural Modulus | ISO 527 | 1600 Mpa | |
| Tensile Modulus | ISO527-2 | 1600 Mpa | |
| Flexural Modulus | ASTM D790/ISO 178 | 1600 kg/cm²(MPa)[Lb/in²] |
| Other | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| purpose | 日用品，工业零配件 |
| Impact Properties | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 3.3 kJ/m² |
| Physical Properties | Test Condition | Test Method | PRIME POLYMER JAPAN/J106G |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 0.910 |