Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PARA 1032 SOLVAY USA
IXEF®
Vehicle electronics、Automotive interior parts、furniture、Metal substitution、Application in the automo、sporting goods、Highlight application
high strength、Creep resistance、60%、glass fibre、Filler: Glass fiber reinf、60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SOLVAY USA/1032 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256 | 900 J/m |
Mechanical properties | Test Condition | Test Method | SOLVAY USA/1032 |
---|---|---|---|
Tensile modulus | ISO 527-2 | 24000 Mpa | |
bending strength | ISO 178 | 400 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
Flexural modulus | ISO 178 | 23500 Mpa | |
tensile strength | 断裂 | ISO 527-2 | 280 Mpa |
Electrical performance | Test Condition | Test Method | SOLVAY USA/1032 |
---|---|---|---|
dielectric strength | IEC 60243-1 | 24 KV/mm | |
Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
dielectric constant | 110Hz | IEC 60250 | 4.50 |
Dissipation Factor | 110Hz | IEC 60250 | 9E-03 |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
flammability | Test Condition | Test Method | SOLVAY USA/1032 |
---|---|---|---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
UL flame retardant rating | UL 94 | HB | |
Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 775 °C |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 825 °C |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 775 °C |
Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 800 °C |
Limiting Oxygen Index | ISO 4589-2 | 25 % | |
Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 800 °C |
physical property | Test Condition | Test Method | SOLVAY USA/1032 |
---|---|---|---|
Water absorption - Ejil, 65% RH | 内部方法 | 1.3 % | |
Shrinkage rate | 内部方法 | 0.10-0.30 % | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.13 % |
density | ISO 1183 | 1.77 g/cm³ |
Thermal performance | Test Condition | Test Method | SOLVAY USA/1032 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 230 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.4E-05 cm/cm/°C |