POM F30-02 E9000 MITSUBISHI ENGINEERING JAPAN
Iupital™ 
Automotive sector、Thin walled components、Application in the automo、Electrical components、Thin walled components、Electronic data processin
wear resistant、Chemical resistance、Thermal stability、Anti creep、Good liquidity、Good forming performance、Low viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F30-02 E9000
Rockwell hardnessM级ASTM D78580
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F30-02 E9000
bending strength23°CASTM D79091.0 Mpa
shear strength2.00mmASTM D73255.0 Mpa
tensile strength 屈服,23°CASTM D63862.0 Mpa
Flexural modulus23°CASTM D7902650 Mpa
elongation断裂,23°CASTM D63840 %
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F30-02 E9000
Volume resistivityASTM D2571E+14 ohms·cm
Surface ResistivityASTM D2571E+16 ohms
Dissipation Factor1MHzASTM D1507E-03
dielectric strengthASTM D14919 KV/mm
dielectric constant1MHzASTM D1503.70
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F30-02 E9000
UL flame retardant rating0.800mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F30-02 E9000
Shrinkage rateMD：3.00mmASTM D9552.0 %
Water absorption rate平衡,23°C,60%RHASTM D5700.22 %
melt mass-flow rateASTM D123827 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F30-02 E9000
Heat distortion temperature1.8MPa,未退火，HDTASTM D648110 °C
0.45MPa,未退火，HDTASTM D648158 °C
熔融温度，HDTASTM D648165 °C
Linear coefficient of thermal expansionMD：20到80°CASTM D6961.3E-04 cm/cm/°C