PA66 6512 NAN YA TAIWAN
--
Automotive sector,Bottle cap,Electronic field,Electrical field
High impact resistance,Toughening
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | NAN YA TAIWAN/6512 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 110 kg·cm/cm(J/M)ft·lb/in | |
| 3.2mm | ASTM D256 | 110 kg.cm/cm | |
| Flexural modulus | ASTM D790 | 18500 kg/cm2 | |
| tensile strength | ASTM D638 | 850 kg/cm2 | |
| Flexural modulus | ASTM D790/ISO 178 | 18500 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 550 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | NAN YA TAIWAN/6512 |
|---|---|---|---|
| Shrinkage rate | 3mm | ASTM D955 | 1.2-1.9 % |
| melt mass-flow rate | 吸水率，24hrs 23℃ | ASTM D570 | 1.25 % |
| 比重 | ASTM D792 | 1.09 -- | |
| notes | 抗冲及快速成型 | ||
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| purpose | 高韧性及抗冲要求的零件用.如网球拍护条.条钉等 |
| Physical properties | Test Condition | Test Method | NAN YA TAIWAN/6512 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.2-1.9 % | |
| density | ASTM D792/ISO 1183 | 1.09 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 1.25 % |
| Thermal performance | Test Condition | Test Method | NAN YA TAIWAN/6512 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 65 ℃（℉） |