POM 500P NC010 POM vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

POM DUPONT USA 500P NC010

Injection grade

US$ 4,720 / MT

FOB Guangzhou port, China

flammability	Test Condition	Test Method	DUPONT USA/500P NC010
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating		1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	22 %
Atomization	G-value(condensate)	ISO 6452	3.5E-04 g
UL flame retardant rating	1.5mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	20 mm/min
Atomization	F-value(refraction)	ISO 6452	90 %
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
mechanical properties	Test Condition	Test Method	DUPONT USA/500P NC010
Tensile creep modulus	1hr	ISO 899-1	2800 Mpa
Tensile modulus		ISO 527-2	3100 Mpa
Nominal tensile fracture strain		ISO 527-2	30 %
Bending modulus		ISO 178	3000 Mpa
Tensile creep modulus	1000hr	ISO 899-1	1600 Mpa
Poisson's ratio		ISO 527	0.35
bending strength	3.5%Strain	ISO 178	80.0 Mpa
Tensile strain	Yield	ISO 527-2	17 %
tensile strength	Yield	ISO 527-2	71.0 Mpa
thermal performance	Test Condition	Test Method	DUPONT USA/500P NC010
Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	9E-08 m²/s
Ball Pressure Test	165°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	TD：AnnealingTemperature	ISO 11359-2	160 °C
Linear coefficient of thermal expansion		TD：--	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
Melting temperature		ISO 11357-3	178 °C
Vicat softening temperature		ISO 306/B50	155 °C
Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
		MD：--	ISO 11359-2	1E-04 cm/cm/°C
		TD：AnnealingTime-Optional	ISO 11359-2	30.0 min/mm
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160 °C
Physical properties	Test Condition	Test Method	DUPONT USA/500P NC010
density		ISO 1183	1.42 g/cm³
Shrinkage rate	MD	ISO 294-4	2.0 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.4 %
Shrinkage rate	TD	ISO 294-4	1.9 %
MediumDensity			1.19 g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.40 %
ThermalConductivityofMelt			0.24 W/m/K
melt mass-flow rate		ISO 1133	15 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	13.0 cm3/10min
Electrical performance	Test Condition	Test Method	DUPONT USA/500P NC010
Dissipation factor	100Hz	IEC 60250	9E-03
Volume resistivity		IEC 60093	2E+14 ohms·cm
Dissipation factor	1MHz	IEC 60250	5.5E-03
Relative permittivity	100Hz	IEC 60250	3.80
Surface resistivity		IEC 60093	4E+14 ohms
Relative permittivity	1MHz	IEC 60250	3.80
Dielectric strength		IEC 60243-1	44 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	DUPONT USA/500P NC010
Rockwell hardness	M-Sale	ISO 2039-2	92
Ball Pressure Test	H358/30	ISO 2039-1	192 Mpa
Rockwell hardness	R-Sale	ISO 2039-2	120
impact performance	Test Condition	Test Method	DUPONT USA/500P NC010
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	280 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	280 kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.00 J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0 kJ/m²
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	2000 N
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	320 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	250 kJ/m²
Supplementary Information	Test Condition	Test Method	DUPONT USA/500P NC010
EmissionofOrganicCompounds		VDA277	3.10 µgC/g
Emission		VDA275	<8.00 mg/kg