LDPE Trithene® TU 3001 Brazil Petroquimica
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Brazil Petroquimica/Trithene® TU 3001 |
|---|---|---|---|
| elongation | TD:断裂,150µm,吹塑薄膜 | ASTM D882 | 740 % |
| Elmendorf tear strength | MD:150µm,吹塑薄膜 | ASTM D1922 | 440 g |
| tensile strength | TD:断裂,150µm,吹塑薄膜 | ASTM D882 | 22.0 MPa |
| Elmendorf tear strength | TD:150µm,吹塑薄膜 | ASTM D1922 | 720 g |
| tensile strength | MD:断裂,150µm,吹塑薄膜 | ASTM D882 | 20.0 MPa |
| elongation | MD:断裂,150µm,吹塑薄膜 | ASTM D882 | 600 % |
| Secant modulus | 5%正割,TD:150µm,吹塑薄膜 | ASTM D882 | 91.0 MPa |
| 5%正割,MD:150µm,吹塑薄膜 | ASTM D882 | 92.0 MPa | |
| Dart impact | 150µm,吹塑薄膜 | ASTM D1709B | 400 g |
| Mechanical properties | Test Condition | Test Method | Brazil Petroquimica/Trithene® TU 3001 |
|---|---|---|---|
| elongation | 断裂,模压成型 | ASTM D638 | 630 % |
| coefficient of friction | 与自身-动态,吹塑薄膜 | ASTM D1894 | 0.40 |
| tensile strength | 屈服,模压成型 | ASTM D638 | 11.0 MPa |
| 断裂,模压成型 | ASTM D638 | 18.0 MPa |
| optical performance | Test Condition | Test Method | Brazil Petroquimica/Trithene® TU 3001 |
|---|---|---|---|
| gloss | 60°,150µm,吹塑薄膜 | ASTM D2457 | 62 |
| Haze ratio | 150µm,吹塑薄膜 | ASTM D1003 | 16 % |
| physical property | Test Condition | Test Method | Brazil Petroquimica/Trithene® TU 3001 |
|---|---|---|---|
| density | ASTM D1505 | 0.923 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.14 g/10min |
| Thermal performance | Test Condition | Test Method | Brazil Petroquimica/Trithene® TU 3001 |
|---|---|---|---|
| vicat | ASTM D1525 | 95.0 °C |