ABS MP-0670 Samsung Cheil South Korea
STAREX®
Automotive Applications、Electrical enclosure
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/MP-0670 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| 23°C | ISO 180/1A | 25 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/MP-0670 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 106 |
| R级 | ASTM D785 | 106 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/MP-0670 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 51.0 Mpa |
| elongation | 断裂 | ASTM D638 | 25 % |
| Tensile modulus | ISO 527-2/50 | 2350 Mpa | |
| bending strength | ISO 178 | 72.0 Mpa | |
| ASTM D790 | 65.0 Mpa | ||
| Flexural modulus | ISO 178 | 2350 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 35.0 Mpa |
| 屈服 | ASTM D638 | 44.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.0 % |
| Flexural modulus | ASTM D790 | 2100 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 37.0 Mpa |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/MP-0670 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 2.3 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20-0.50 % |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 2.3 g/10min |
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.20-0.50 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.30 % |
| 平衡,23°C,50%RH | ISO 62 | 0.30 % | |
| Shrinkage rate | TD：3.20mm | ASTM D955 | 0.20-0.50 % |
| MD:3.20mm | ISO 2577 | 0.20-0.50 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/MP-0670 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 80.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 88.0 °C | |
| vicat | -- | ISO 306/B120 | 101 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 93.0 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 96.0 °C | |
| vicat | -- | ISO 306/B50 | 100 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 100 °C |