Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC TAROLON 2500 G2 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROLON 2500 G2 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 150 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROLON 2500 G2 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 3600 MPa | |
| elongation | 断裂 | ASTMD638 | 6.0 % |
| bending strength | --2 | ISO 178 | 100 MPa |
| 屈服 | ASTM D790 | 105 MPa | |
| 断裂 | ASTM D790 | 100 MPa | |
| Tensile modulus | ASTMD638 | 3800 MPa | |
| tensile strength | 断裂 | ASTMD638 | 70.0 MPa |
| 屈服 | ASTMD638 | 75.0 MPa | |
| bending strength | --3 | ISO 178 | 105 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLON 2500 G2 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
| dielectric strength | 2.00mm | ASTM D149 | 22 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 4 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROLON 2500 G2 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 3.2mm | UL 94 | V-1 |
| 1.6mm | UL 94 | V-2 | |
| Limiting Oxygen Index | ASTM D2863 | 30 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROLON 2500 G2 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30to0.50 % |
| Water absorption rate | 饱和 | ASTM D570 | 0.30 % |
| density | ASTMD792 | 1.24to1.26 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.080 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 12 g/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLON 2500 G2 |
|---|---|---|---|
| vicat | ISO 306/A50 | 153 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 142 °C |
| ball-indentation hardness | 125°C | VDE0470 | 通过 |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 3.5E-05 cm/cm/°C |
| Continuous use temperature | IEC 60216 | 130 °C |