Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PPO EN185-701 SABIC INNOVATIVE US
NORYL™
electromagnetic shielding
Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
Impact strength of cantilever beam gap | -40°C | ASTM D256 | 160 J/m |
23°C | ASTM D256 | 390 J/m | |
Dart impact | -30°C | ASTM D3029 | 24.0 J |
-40°C | ASTM D3029 | 13.0 J |
hardness | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
Rockwell hardness | R 级 | ASTM D785 | 113 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 50 % |
bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 67.0 Mpa |
tensile strength | 屈服 | ASTM D638 | 42.0 Mpa |
Flexural modulus | 100 mm 跨距 | ASTM D790 | 2270 Mpa |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
dielectric strength | 3.20 mm, in Oil | ASTM D149 | 25 KV/mm |
Dissipation Factor | 1 MHz | IEC 60250 | 3.5E-3 |
dielectric constant | 60 Hz | ASTM D150 | 2.80 |
Dissipation Factor | 60 Hz | ASTM D150 | 4.0E-3 |
50 Hz | ASTM D150 | 4.0E-3 | |
Hot wire ignition (HWI) | UL 746 | PLC 1 | |
arc resistance | ASTM D495 | PLC 7 | |
High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
High arc combustion index (HAI) | UL 746 | PLC 0 | |
dielectric constant | 50 kHz | ASTM D150 | 2.80 |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
UL flame retardant rating | 3.0 mm | UL 94 | V-0 |
1.5 mm | UL 94 | V-1 | |
Radiation board grade | UL Unspecified | TRUE |
squeeze out | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
drying temperature | 90 to 100 °C | ||
Melt Temperature | 195 to 210 °C | ||
die temperature | 205 °C | ||
Joint temperature | 205 °C | ||
drying time | 2.0 to 4.0 hr | ||
Suggested maximum moisture content | 0.020 % | ||
Temperature in Zone 2 of the material cylinder | 170 °C | ||
Temperature in Zone 4 of the material cylinder | 190 °C | ||
Temperature in Zone 3 of the material cylinder | 190 °C | ||
Temperature in Zone 1 of the material cylinder | 170 °C |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
Water absorption rate | 24 hr | ASTM D570 | 0.070 % |
density | ASTM D792 | 1.08 g/cm³ |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EN185-701 |
---|---|---|---|
Linear coefficient of thermal expansion | -40 到 95°C,流动 | ASTM E831 | 7.4E-5 cm/cm/°C |
Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm,HDT | ASTM D648 | 82.0 °C |
RTI Imp | UL 746 | 50.0 °C | |
RTI | UL 746 | 50.0 °C | |
Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm,HDT | ASTM D648 | 93.0 °C |
RTI Elec | UL 746 | 50.0 °C |