PC Iupilon® MB5002R Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® MB5002R
Charpy Notched Impact Strength23°CISO 17980 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® MB5002R
Nominal tensile fracture strainISO 527-2140 %
Tensile modulusISO 527-22100 MPa
Tensile strain屈服ISO 527-25.9 %
tensile strength 屈服ISO 527-250.0 MPa
Flexural modulusISO 1782000 MPa
bending strengthISO 17878.0 MPa
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® MB5002R
dielectric strength3.00mmIEC 60243-118 kV/mm
Volume resistivityIEC 600933E+13 ohms·cm
relative permittivity100HzIEC 602504.40
Dissipation Factor100HzIEC 602508.1E-03
dielectric strength2.00mmIEC 60243-124 kV/mm
relative permittivity1MHzIEC 602503.50
Surface ResistivityIEC 600937E+11 ohms
Dissipation Factor1MHzIEC 602500.023
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® MB5002R
Shrinkage rateTD:3.20mm0.60to0.80 %
Melt volume flow rate300°C/1.2kgISO 11339.20 cm³/10min
Shrinkage rateMD:3.20mm0.60to0.80 %
Water absorption rate饱和,23°CISO 620.20 %
densityISO 11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO 113310 g/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® MB5002R
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B132 °C
1.8MPa,未退火，HDTISO 75-2/A112 °C
Linear coefficient of thermal expansionMDISO 11359-28E-05 cm/cm/°C
TDISO 11359-29.6E-05 cm/cm/°C