Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1201 10P LG CHEM KOREA
LUPOY®
Toy、Food containers、chip、bottle
transparent、wear resistant、Low viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 无断裂 |
| Dart impact | 23°C, 3.20 mm, Total Energy | ASTM D3763 | 87.0 J |
| hardness | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 73 |
| R 级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2410 Mpa | |
| tensile strength | 屈服, 23°C2 | ASTM D638 | 60.0 Mpa |
| elongation | 断裂 | ASTM D638 | 150 % |
| 屈服 | ASTM D638 | 6.0 % | |
| bending strength | ASTM D790 | 96.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 71.0 Mpa |
| Wear resistance - Change in Haze | ASTM D1004 | 45 % | |
| Flexural modulus | ASTM D790 | 2410 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| dielectric constant | 60 Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.0E-3 |
| Volume resistivity | 23°C | ASTM D257 | 2.0E+17 ohms·cm |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | 2.00 mm | IEC 60112 | PLC 2 |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70 to 1.5 % |
| flammability | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| Hot filament ignition temperature | 2.0 mm | IEC 60695-2-13 | 850 °C |
| Average degree of combustion | ASTM D746 | 3 CM | |
| Limiting Oxygen Index | ASTM D2863 | 26 % |
| physical property | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.15 % |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.32 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Shrinkage rate | Flow | ASTM D955 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/1201 10P |
|---|---|---|---|
| Linear coefficient of thermal expansion | -40 到 82°C，流动 | ASTM D696 | 6.8E-5 cm/cm/°C |
| Ball pressure temperature | IEC 60598-1 | > 125 °C | |
| vicat | ASTM D15256 | 149 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm，HDT | ASTM D648 | 128 °C |
| 1.8 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 141 °C | |
| 0.45 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 144 °C |