Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Copolymer TRANSMARE® 14CGF50-0.001 Transmare Compounding B.V.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CGF50-0.001 |
|---|---|---|---|
| Charpy Notched Impact Strength | -20°C | ISO 179/A | 12 kJ/m² |
| -40°C | ISO 179/A | 12 kJ/m² | |
| Impact strength of cantilever beam gap | 0°C | ISO 180/A | 18 kJ/m² |
| Charpy Notched Impact Strength | 0°C | ISO 179/A | 14 kJ/m² |
| 23°C | ISO 179/A | 19 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/A | 13 kJ/m² |
| 23°C | ISO 180/A | 20 kJ/m² | |
| -20°C | ISO 180/A | 17 kJ/m² |
| hardness | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CGF50-0.001 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 71 |
| Mechanical properties | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CGF50-0.001 |
|---|---|---|---|
| tensile strength | 断裂,4.00mm | ISO 527-2/50 | 90.0 MPa |
| Tensile strain | 断裂,4.00mm | ISO 527-2/50 | 4.0 % |
| Flexural modulus | ISO 178 | 9900 MPa | |
| tensile strength | 屈服,4.00mm | ISO 527-2/50 | 90.0 MPa |
| bending strength | ISO 178 | 130 MPa | |
| Tensile strain | 屈服,4.00mm | ISO 527-2/50 | 3.5 % |
| physical property | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CGF50-0.001 |
|---|---|---|---|
| density | ISO 1183 | 1.33 g/cm³ | |
| melt mass-flow rate | 230°C/5.0kg | ISO 1133 | 12 g/10min |
| 230°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 14CGF50-0.001 |
|---|---|---|---|
| vicat | ISO 306/A | 158 °C |