Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A400M D1 TORAY JAPAN
Torelina®
Electrical applications
Glass fiber reinforced、Flame retardant、Filler: Glass mineral、55% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 30 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 115 mm |
| hardness | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 122 |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| Shore hardness | ASTM D-785 | 122 洛氏 | |
| coefficient of friction | 对钢 | ASTM D-1894 | 0.28 |
| Impact strength of cantilever beam gap | 无缺口23℃ | ASTM D-256 | 25 KJ/m |
| bending strength | ASTM D-790 | 190 Mpa | |
| abrasion | ASTM D-1044 | 70 mg/1000回 | |
| tensile strength | ASTM D-638 | 145 Mpa | |
| limiting pv value | 东丽法 | 815 KJ/m | |
| bending strength | ASTM D-790 | 15.1 GPa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.3 % |
| Impact strength of cantilever beam gap | 缺口23℃ | ASTM D-256 | 100 J/m |
| bending strength | 23°C | ISO 178 | 255 Mpa |
| tensile strength | ASTM D-638 | 1.3 % | |
| elongation at break | ASTM D-732 | 65 | |
| tensile strength | 屈服,23°C | ISO 527-2 | 170 Mpa |
| Flexural modulus | 23°C | ISO 178 | 18500 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | IEC 60250 | 4.90 |
| dielectric strength | ASTM D-149 | 15 MV/m | |
| IEC 60243-1 | 22 KV/mm | ||
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Induced positive connection | 10 | ASTM D-150 | 0.002 |
| Inherent resistance of volume | ASTM D-257 | 10 Ω.m | |
| arc resistance | W电极 | ASTM D-495 | 128 秒 |
| dielectric constant | 10 | ASTM D-150 | 5.0 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 2E-03 |
| flammability | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| UL flame retardant rating | 0.36mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| Shrinkage rate | 流动方向 | 东丽法 | 0.15 % |
| TD:3.00mm2 | 内部方法 | 0.75 % | |
| MD:3.00mm4 | 内部方法 | 0.16 % | |
| 320℃,98MPa,1mm厚，流动长 | 东丽法 | 110 | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Shrinkage rate | 垂重方向 | 东丽法 | 0.55 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A400M D1 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Linear coefficient of thermal expansion | 垂重方向 | ASTM D-696 | 2.5 |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | >260 °C |
| combustibility | UL -94 | V-0 | |
| Linear coefficient of thermal expansion | 流动方向 | ASTM D-696 | 1.7 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| melting temperature | DSC | 278 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 3E-05 cm/cm/°C |