Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/MXD6 1022H GY553 MITSUBISHI ENGINEERING JAPAN
RENY™
Automotive sector、Electronic field、Electrical field
Glass fiber reinforced、Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1022H GY553 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.647to20.893 |
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.222to0.332 |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1022H GY553 |
|---|---|---|---|
| dielectric strength | 23℃ | V/mil | 500to840 |
| Surface Resistivity | ohms | 5.0E+3-6.0E+15 | |
| Compared to the Leakage Tracking Index (CTI) | V | ||
| Volume resistivity | 23℃ | ohms·cm | 3.0E+2-2.1E+16 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1022H GY553 |
|---|---|---|---|
| Yield, 23 ℃ | % | 2.0to3.0 | |
| Fracture, 23 ℃ | 151.72to280.69 MPa | ||
| % | 1.6to2.1 |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1022H GY553 |
|---|---|---|---|
| Hot filament ignition temperature | °C | 798to904 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1022H GY553 |
|---|---|---|---|
| Balance, 23 ℃, 50% RH | % | 0.70to1.5 | |
| melt mass-flow rate | 275°C/2.16kg | g/10min | 3.6to20 |
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 38.1E-3-78.7E-3 |
| Saturation, 23 ℃ | % | 0.060to0.15 | |
| Melt volume flow rate | 275°C/2.16kg | ISO 527-2/5 | 0.01to0.04 |
| 23℃,24hr | % | 0.16to0.30 |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1022H GY553 |
|---|---|---|---|
| 0.45MPa, Not annealed | °C | 234to255 | |
| flow | mm/mm/°C | 137.2E-5-25.4E-5 | |
| 1.8MPa, Not annealed | °C | 223to230 | |
| horizontal | mm/mm/°C | 55.9E-5-50.8E-5 |