PCTG FX200 PCTG vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PCTG EASTMAN USA FX200

Injection grade

US$ 4,470 / MT

FOB Shenzhen Port

thermal performance	Test Condition	Test Method	EASTMAN USA/FX200
specific heat	250°C	DSC	2600 J/kg/°C
Linear coefficient of thermal expansion	MD：23°C	ASTM D696	8E-05 cm/cm/°C
specific heat	60°C	DSC	1700 J/kg/°C
		100°C	DSC	1900 J/kg/°C
		200°C	DSC	2400 J/kg/°C
		150°C	DSC	2300 J/kg/°C
Melting temperature			119 °C
film	Test Condition	Test Method	EASTMAN USA/FX200
Tensile strain TD	Yield,250μm	ASTM D882	8.0 %
PPTTearResistance	MD:23°C,250.0μm		40 N
tear strength	TD:23°C,250.0μm	ASTM D1938	200 gf
Secant modulus	250μm，MD	ASTM D882	1500 Mpa
Oxygen permeability	23°C,250μm,50%RH	ASTM D3985	44 cm³·mm/m²/atm/24hr
tear strength	MD:23°C,250.0μm	ASTM D1938	310 gf
Water vapor permeability	23°C,100%RH,250μm	ASTMF1249	4.0 g/m²/24hr
tensile strength	Yield,250μm，TD	ASTM D882	41.0 Mpa
Elmendorf tear strength	TD:23°C,250.0μm	ASTM D1922	4 N
Tensile strain TD	Break,250μm	ASTM D882	120 %
Carbon dioxide transmittance	23°C,254.0μm	ASTM D1434	210 cm³·mm/m²/atm/24hr
elongation	Break,250μm，MD	ASTM D882	110 %
Elmendorf tear strength	MD:23°C,250.0μm	ASTM D1922	4 N
Tear resistance of pants type	TD:250μm	ISO 6383-1	9.00 N/mm
tensile strength	Break,250μm，MD	ASTM D882	57.0 Mpa
Tear resistance of pants type	MD:250μm	ISO 6383-1	10.0 N/mm
Thin film puncture strength	250μm	ASTM D3763	4.50 J
Dart impact	-30°C,250μm	ASTM D1709A	830 g
tensile strength	Yield,250μm，MD	ASTM D882	43.0 Mpa
Tensile strain	Yield,250μm，MD	ASTM D882	8.0 %
Dart impact	-18°C,250μm	ASTM D1709A	830 g
Water vapor permeability	38°C,100%RH,250μm	ASTMF1249	10 g/m²/24hr
PPTTearResistance	TD:23°C,250.0μm		40 N
Secant modulus	250μm，TD	ASTM D882	1400 Mpa
film thickness			250 µm
Dart impact	23°C,250μm	ASTM D1709A	830 g
tensile strength	Break,250μm，TD	ASTM D882	42.0 Mpa
Physical properties	Test Condition	Test Method	EASTMAN USA/FX200
Water absorption rate	23°C,24hr,0.254mm	ASTM D570	0.50 %
optical performance	Test Condition	Test Method	EASTMAN USA/FX200
Huangdu Index	250mm	ASTM D1925	0.50 YI
Transmittance rate	250μm	ASTM D1003	93.0 %
turbidity	250μm	ASTM D1003	0.80 %
gloss	60°,250μm	ASTM D2457	158
Transmittance rate	250.0μm，UV		89 %
Refractive index		ASTM D542	1.540
mechanical properties	Test Condition	Test Method	EASTMAN USA/FX200
Taber wear resistance	23°C,250.0μm	ASTM D1044	20Haze %
Supplementary Information	Test Condition	Test Method	EASTMAN USA/FX200
SurfaceEnergy	Dispersive:23°C,250.0μm	ASTM D5946	39 dyne/cm
		Total:23°C,250.0μm	ASTM D5946	47 dyne/cm
		Polar:23°C,250.0μm	ASTM D5946	8 dyne/cm
elastomer	Test Condition	Test Method	EASTMAN USA/FX200
tear strength	Split7	ASTM D1938	10 kN/m
tear strength		Split6	ASTM D1938	9.0 kN/m