Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PCTG FX200 EASTMAN USA
Tritan™
Electrical applications、Household daily necessiti
Chemical resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical performance | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| Tab | 23°C,250.0µm | ASTMD1044 | 20Haze % |
| elastomer | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| tear strength | 开裂6 | ASTMD1938 | 9.0 kN/m |
| 开裂7 | ASTMD1938 | 10 kN/m |
| Supplementary Information | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| SurfaceEnergy | Polar:23°C,250.0µm | ASTMD5946 | 8 dyne/cm |
| Total:23°C,250.0µm | ASTMD5946 | 47 dyne/cm | |
| Dispersive:23°C,250.0µm | ASTMD5946 | 39 dyne/cm |
| physical property | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr,0.254mm | ASTMD570 | 0.50 % |
| optical performance | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| Light transmittance | 250µm | ASTMD1003 | 93.0 % |
| Haze | 250µm | ASTMD1003 | 0.80 % |
| Refractive index | ASTMD542 | 1.540 | |
| gloss | 60°,250µm | ASTMD2457 | 158 |
| Huangdu Index | 250mm | ASTMD1925 | 0.50 YI |
| Light transmittance | 250.0µm，UV | 89 % |
| film | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| Elongation MD | 断裂,250µm | ASTMD882 | 110 % |
| Hammer impact 4 | -30°C,250µm | ASTMD1709A | 830 g |
| 23°C,250µm | ASTMD1709A | 830 g | |
| Tear resistance of pants type 5 | TD:250µm | ISO6383-1 | 9.00 N/mm |
| Tensile strain MD | Yield,250µm | ASTMD882 | 8.0 % |
| CarbonDioxidePermeability | 23°C,254.0µm | ASTMD1434 | 210 cm³·mm/m²/atm/24hr |
| Hammer impact 4 | -18°C,250µm | ASTMD1709A | 830 g |
| Tear resistant ductility | MD:23°C,250.0µm | ASTMD1938 | 310 gf |
| Elmondov tear strength | MD:23°C,250.0µm | ASTMD1922 | 4 N |
| Tear resistance of pants type 5 | MD:250µm | ISO6383-1 | 10.0 N/mm |
| Water vapor permeability | 38°C,100%RH,250µm | ASTMF1249 | 10 g/m²/24hr |
| Tensile strain TD | Break,250µm | ASTMD882 | 120 % |
| PPTTearResistance | MD:23°C,250.0µm | 40 N | |
| Secant modulus MD | 250µm | ASTMD882 | 1500 Mpa |
| Tensile strength MD | 屈服,250µm | ASTMD882 | 43.0 Mpa |
| Tensile strength TD | Yield,250µm | ASTMD882 | 41.0 Mpa |
| Elmondov tear strength | TD:23°C,250.0µm | ASTMD1922 | 4 N |
| Film thickness - tested | 250 µm | ||
| Tensile strength MD | Break,250µm | ASTMD882 | 57.0 Mpa |
| PPTTearResistance | TD:23°C,250.0µm | 40 N | |
| Tear resistant ductility | TD:23°C,250.0µm | ASTMD1938 | 200 gf |
| Tensile strength TD | Break,250µm | ASTMD882 | 42.0 Mpa |
| Membrane puncture strength 3 | 250µm | ASTMD3763 | 4.50 J |
| Water vapor permeability | 23°C,100%RH,250µm | ASTMF1249 | 4.0 g/m²/24hr |
| Tensile strain TD | Yield,250µm | ASTMD882 | 8.0 % |
| Secant modulus TD | 250µm | ASTMD882 | 1400 Mpa |
| Oxygen permeability rate | 23°C,250µm,50%RH | ASTMD3985 | 44 cm³·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/FX200 |
|---|---|---|---|
| specific heat | 60°C | DSC | 1700 J/kg/°C |
| 150°C | DSC | 2300 J/kg/°C | |
| 200°C | DSC | 2400 J/kg/°C | |
| 100°C | DSC | 1900 J/kg/°C | |
| Linear coefficient of thermal expansion | MD：23°C | ASTMD696 | 8E-05 cm/cm/°C |
| specific heat | 250°C | DSC | 2600 J/kg/°C |
| Melting temperature | 119 °C |