Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM FG2020-E9000-BK MITSUBISHI ENGINEERING JAPAN
Iupital™
Automotive sector、Electronic and Electrical
wear resistant、High mobility、Good wear resistance、Good wear resistance、Medium to high viscosity、Good wear resistance, goo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FG2020-E9000-BK |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Basic performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FG2020-E9000-BK |
|---|---|---|---|
| Shrinkage rate | flow,2.00MM | ASTM D955 | 0.50 % |
| melt mass-flow rate | 190℃/2.16kg | ASTM D1238 | 6.5 g/10 min |
| Water absorption rate | Equilibrium,23℃,60%rh | ASTM D570 | 0.20 % |
| density | ASTM D792 | 1.58 g/cm³ |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FG2020-E9000-BK |
|---|---|---|---|
| tensile strength | Yield,23℃ | ASTM D638 | 120 MPa |
| bending strength | 23°C | ASTM D790 | 157 MPa |
| Flexural modulus | 23°C | ASTM D790 | 6680 MPa |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 57.0 J/m |
| elongation | Break,23℃ | ASTM D638 | 2.0 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FG2020-E9000-BK |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohm·cm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FG2020-E9000-BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 164 °C |
| melting temperature | ASTM D3418 | 165 °C |