PES 3601GL20 SUMITOMO JAPAN
SUMIKAEXCEL®
--
Filler: Glass fiber reinf、20% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 6.40mm | ASTM D256 | 430 J/m |
| hardness | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 134 |
| Electrical performance | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| arc resistance | ASTM D495 | 150 sec |
| Mechanical properties | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ASTM D790 | 172 Mpa | |
| Flexural modulus | ASTM D790 | 5900 Mpa | |
| tensile strength | ASTM D638 | 124 Mpa |
| flammability | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| UL flame retardant rating | 0.43mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.36 % |
| Shrinkage rate | TD | ASTM D955 | 0.40 % |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/3601GL20 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 210 °C |
| Linear coefficient of thermal expansion | TD:50到150°C | ASTM D696 | 4.8E-05 cm/cm/°C |
| MD:-50到150°C | ASTM D696 | 2.6E-05 cm/cm/°C |