Epoxy INSULCAST® 136/INSULCURE 11B ITW FORMEX
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
Shore hardness | 邵氏D | ASTM D2240 | 89 |
Electrical performance | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
Dissipation Factor | 1kHz | ASTM D150 | 0.020 |
Volume resistivity | ASTM D257 | 5E+16 ohms·cm | |
dielectric strength | ASTM D149 | 17 kV/mm | |
dielectric constant | 1kHz | ASTM D150 | 4.80 |
Mechanical properties | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 2.0to4.0 % |
tensile strength | ASTM D638 | 70.3 MPa | |
compressive strength | ASTM D695 | 107 MPa | |
bending strength | ASTM D790 | 117 MPa |
thermosetting | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
Thermosetting components | 按重量计算的混合比 | 100 | |
后固化时间(150°C) | 1.0 hr | ||
硬化法 | 按重量计算的混合比:9.0到10 | ||
贮藏期限 | 52 wk |
Uncured Properties | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
density | --2 | 0.948 g/cm³ | |
--3 | 1.59 g/cm³ | ||
Viscosity | --3 | ASTM D2393 | 80 Pa·s |
--4 | ASTM D2393 | 25 Pa·s | |
固化时间(100°C) | ASTM D2393 | 2.0 hr | |
--2 | ASTM D2393 | 0.70 Pa·s | |
Color | --2 | Amber | |
Viscosity | 储存稳定性(25°C) | ASTM D2393 | 150 min |
Color | --3 | Black |
Cured Properties | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
Shrinkage rate | 0.20 % |
Thermal performance | Test Condition | Test Method | ITW FORMEX/INSULCAST® 136/INSULCURE 11B |
---|---|---|---|
Heat distortion temperature | HDT | 155 °C | |
thermal conductivity | 0.72 W/m/K | ||
Usage temperature | 155 °C | ||
Linear coefficient of thermal expansion | MD | 4E-05 cm/cm/°C |