Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC G-3130 TEIJIN JAPAN
PANLITE®
Camera applications
Anti creep,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| Water absorption rate | 24hr,23℃ | ASTM D-570 | 0.12 % |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| Tensile modulus | ASTM D-638 | 8240(84000) MPa(Kgf/cm | |
| bending strength | ASTM D790/ISO 178 | 186(1900) kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 7260(74000) kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D-785 | 93 M标度 | |
| Shrinkage rate | 垂直方向 | ASTM D-955 | 0.3-0.5 % |
| Impact strength of cantilever beam gap | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 160(16) J/m(kgf·cm/cm) |
| compressive strength | ASTM D-695 | 157(1600) MPa(Kgf/cm | |
| elongation at break | ASTM D638/ISO 527 | 3.5 % | |
| tensile strength | ASTM D638/ISO 527 | 126(1280) kg/cm²(MPa)[Lb/in²] | |
| Shrinkage rate | 流动方向 | ASTM D-955 | 0.02-0.2 % |
| bending strength | ASTM D-790 | 186(1900) MPa(Kgf/cm | |
| elongation | 断裂 | ASTM D-638 | 3.5 |
| tensile strength | 断裂点 | ASTM D-638 | 126(1280) MPa(Kgf/cm |
| Tensile modulus | ASTM D638/ISO 527 | 8240(84000) kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 160(16) kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | ASTM D-790 | 7260(74000) MPa(Kgf/cm |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 1 | |
| dielectric constant | 60Hz | ASTM D-150 | 3.51 |
| Dielectric loss | 10，正切 | ASTM D-150 | 0.009 |
| Conductive Track Resistance (CTI) | IEC 112 | 180 V | |
| arc resistance | ASTM D-495 | sec sec | |
| Dielectric loss | 60Hz，正切 | ASTM D-150 | 0.0008 |
| dielectric strength | 快速加压值厚度1.6mm | ASTM D-149 | 30 KV/mm |
| Impact strength of cantilever beam gap | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 160(16) J/m(kgf·cm/cm) |
| dielectric constant | 10 | ASTM D-150 | 3.41 |
| other | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| characteristic | 电器.电子元件 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.43 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.12 % |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| transmittance | 厚度3mm | ASTM D-1003 | 半透明 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/G-3130 |
|---|---|---|---|
| TEMPERATURE | 电学式，厚度1.47mm | UL 746B | 130 °C |
| Linear coefficient of thermal expansion | 垂直方向 | ASTM D-696 | 5.6 |
| 流动方向 | ASTM D-696 | 2.0 | |
| TEMPERATURE | 非冲击式，厚度1.47mm | UL 746B | 130 °C |
| Heat distortion temperature | 负荷0.451MPa(4.6kgf/cm)，HDT | ASTM D-648 | 151 °C |
| TEMPERATURE | 冲击式，厚度1.47mm | UL 746B | 125 °C |
| Heat distortion temperature | 负荷1.813MPa(18.6kgf/cm)，HDT | ASTM D-648 | 149 °C |