Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XHT3143 BK SABIC INNOVATIVE US
LEXAN™
Lighting applications、Automotive External Parts、Architectural Application
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XHT3143 BK |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 6.0E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTM D152510, ISO 306/B12010 | 170 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 6.0E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 6.0E-5 cm/cm/°C | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 168 °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 152 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 156 °C | |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 166 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/XHT3143 BK |
|---|---|---|---|
| Middle Temperature | 280 到 310 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 135 °C | ||
| Mold Temperature | 95 到 130 °C | ||
| Vent Depth | 0.025 到 0.080 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 290 到 325 °C | ||
| Rear Temperature | 270 到 300 °C | ||
| Nozzle Temperature | 285 到 320 °C | ||
| Front Temperature | 290 到 325 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 90 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/XHT3143 BK |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.30 % |
| Melt Mass-Flow Rate | 330°C/2.16 kg | ASTM D1238 | 33 g/10 min |
| Melt Volume flow Rate | 330°C/2.16 kg | ISO 1133 | 30.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.60 到 0.90 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.30 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XHT3143 BK |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2500 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 70 % |
| Tensile Strength | 屈服 3 | ASTM D638 | 70.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2600 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 2700 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 70.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 120 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 6.0 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 80.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2500 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 70 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 55.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XHT3143 BK |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 68.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| 23°C | ISO 179/1eA | 11 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |