Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PS+PA NORYL GTX™ GTX979 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX979 resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C9 | ISO 180/1A | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 150 J/m |
| 23°C | ASTM D256 | 220 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C9 | ISO 180/1A | 17 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| -30°C | ISO 180/1U | 无断裂 |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX979 resin |
|---|---|---|---|
| Volume resistivity | 内部方法 | 1.0E+3到1.0E+4 ohms·cm |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL GTX™ GTX979 resin |
|---|---|---|---|
| elongation | 断裂4 | ASTM D638 | 60 % |
| tensile strength | 屈服4 | ASTM D638 | 55.0 MPa |
| Flexural modulus | --6 | ISO 178 | 2150 MPa |
| elongation | 断裂 | ISO 527-2/50 | 30 % |
| Tensile modulus | -- | ISO 527-2/1 | 2100 MPa |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 80.0 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 MPa |
| bending strength | --6,7 | ISO 178 | 80.0 MPa |
| elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| 屈服4 | ASTM D638 | 5.0 % | |
| Tensile modulus | --3 | ASTM D638 | 2000 MPa |
| tensile strength | 断裂4 | ASTM D638 | 50.0 MPa |
| 断裂 | ISO 527-2/50 | 50.0 MPa | |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2050 MPa |
| flammability | Test Condition | Test Method | SABIC/NORYL GTX™ GTX979 resin |
|---|---|---|---|
| Burning wire flammability index | 3.2mm | IEC 60695-2-12 | 650 °C |
| physical property | Test Condition | Test Method | SABIC/NORYL GTX™ GTX979 resin |
|---|---|---|---|
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 11.0 cm³/10min |
| density | ASTMD792 | 1.08 g/cm³ | |
| Shrinkage rate | MD:3.20mm | 内部方法 | 1.2to1.6 % |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 15 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.2 % |
| 饱和,23°C | ISO 62 | 4.2 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 1.2to1.6 % |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX979 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 9.6E-05 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 182 °C |
| Heat distortion temperature | 0.45MPa,未退火,100mm跨距10，HDT | ISO 75-2/Be | 178 °C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| MD:23到80°C | ISO 11359-2 | 9.6E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 185 °C |
| vicat | -- | ASTMD152511 | 180 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 9.5E-05 cm/cm/°C |