LDPE HP4024W SABIC SAUDI
SABIC®
Laundry bag、film、chip
low density、Low friction coefficient、Smoothness、optical performance 、Anti caking property、Food contact compliance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Supplementary Information | Test Condition | Test Method | SABIC SAUDI/HP4024W |
---|---|---|---|
Inflation ratio (BUR) | 2.00to3.00 |
film | Test Condition | Test Method | SABIC SAUDI/HP4024W |
---|---|---|---|
Dart impact | 50µm,吹塑薄膜 | ASTM D1709 | 100 g |
film thickness | 15-40micron | ||
elongation | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 300 % |
tensile strength | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 19.0 Mpa |
film thickness | 50 µm | ||
elongation | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 600 % |
tensile strength | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 16.0 Mpa |
Mechanical properties | Test Condition | Test Method | SABIC SAUDI/HP4024W |
---|---|---|---|
tensile strength | 屈服,0.0500mm | ISO 527-2 | 11.0 Mpa |
coefficient of friction | ISO 8295 | <20 % | |
Tensile modulus | 0.0500mm | ISO 527-2 | 260 Mpa |
optical performance | Test Condition | Test Method | SABIC SAUDI/HP4024W |
---|---|---|---|
gloss | 20°,50.0µm,吹塑薄膜 | ASTM D2457 | >50 |
Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | <9.0 % |
gloss | 60°,50.0µm,吹塑薄膜 | ASTM D2457 | >100 |
physical property | Test Condition | Test Method | SABIC SAUDI/HP4024W |
---|---|---|---|
density | 23°C | ISO 1183 | 0.923 g/cm³ |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 4.0 g/10min |
Thermal performance | Test Condition | Test Method | SABIC SAUDI/HP4024W |
---|---|---|---|
vicat | ISO 306/A50 | 92.0 °C | |
melting temperature | ISO 3146 | 111 °C |