Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA A-4133L BK324 SOLVAY USA
AMODEL®
Shell、Vehicle electronics、currency、Lawn and garden equipment、Laptop case、Industrial components、Valves/valve components、Metal substitution、Industrial applications、Thick wall accessories (c、Phone、Application in the automo、Machine/mechanical compon、Electrical/Electronic App、Parts under the hood of a
Chemical resistance、Low moisture absorption、Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 59 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 67 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| Tensile modulus | 175°C | ISO 527-2 | 4830 Mpa |
| 23°C | ISO 527-2 | 12600 Mpa | |
| tensile strength | 断裂,23°C | ISO 527-2 | 211 Mpa |
| 断裂,24°C | ISO 527-2 | 125 Mpa | |
| bending strength | 175°C | ISO 178 | 99.3 Mpa |
| Flexural modulus | ASTM D790 | 11000 Mpa | |
| Tensile modulus | 150°C | ISO 527-2 | 5310 Mpa |
| bending strength | 150°C | ISO 178 | 111 Mpa |
| 100°C | ISO 178 | 177 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| tensile strength | 断裂,150°C | ISO 527-2 | 87.6 Mpa |
| Flexural modulus | 23°C | ISO 178 | 10400 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2 | 6.6 % |
| bending strength | ASTM D790 | 290 Mpa | |
| Flexural modulus | 100°C | ISO 178 | 7170 Mpa |
| Tensile strain | 断裂,175°C | ISO 527-2 | 6.6 % |
| tensile strength | 断裂,175°C | ISO 527-2 | 79.3 Mpa |
| Tensile modulus | 100°C | ISO 527-2 | 6830 Mpa |
| tensile strength | ASTM D638 | 200 Mpa | |
| Tensile strain | 断裂,24°C | ISO 527-2 | 4.3 % |
| Tensile modulus | ASTM D638 | 11700 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.6 % |
| Flexural modulus | 150°C | ISO 178 | 4620 Mpa |
| bending strength | 23°C | ISO 178 | 296 Mpa |
| Flexural modulus | 175°C | ISO 178 | 4210 Mpa |
| shear strength | ASTM D732 | 89.6 Mpa | |
| Poisson's ratio | 7.58 0.41 | ||
| compressive strength | ASTM D695 | 179 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 4E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.80 |
| Volume resistivity | ASTM D257 | 2E+16 ohms·cm | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | mm/min |
| Dissipation Factor | 1MHz | ASTM D150 | 0.012 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | V |
| dielectric constant | 1MHz | ASTM D150 | 3.60 |
| dielectric strength | 1.60mm | ASTM D149 | 20 KV/mm |
| optical performance | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| transmissivity | 940nm:1.60mm | ASTM D1003 | >20 % |
| 1070nm:1.60mm | ASTM D1003 | >20 % |
| flammability | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50 % |
| Water absorption rate | 24hr | ASTM D570 | 0.29 % |
| Shrinkage rate | TD | ASTM D955 | 1.0 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/A-4133L BK324 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 327 °C | |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火,3.20mm，HDT | ASTM D648 | 300 °C |
| 0.45MPa,Annealed,3.20mm，HDT | ASTM D648 | 320 °C | |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.5E-05 cm/cm/°C |
| TD：0to100°C | ASTME831 | 7.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 294 °C |
| melting temperature | ASTM D570 | 327 °C | |
| Continuous use temperature | ASTM D3045 | 210 °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2E-05 cm/cm/°C |