Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP RAMOFIN PPH301G6NT POLYRAM ISRAEL
RAMOFIN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/RAMOFIN PPH301G6NT |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 6000 Mpa | |
| ISO 527-2 | 6000 Mpa | ||
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ISO 178 | 105 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 5700 Mpa | |
| bending strength | ASTM D790 | 105 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 90.0 Mpa |
| 屈服 | ISO 527-2 | 90.0 Mpa | |
| Flexural modulus | ASTM D790 | 5700 Mpa |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/RAMOFIN PPH301G6NT |
|---|---|---|---|
| burning rate | FMVSS302 | 9.0 mm/min | |
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/RAMOFIN PPH301G6NT |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.10-0.40 % | |
| MD | ASTM D955 | 0.10-0.40 % | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 3.5 g/10min |
| 230°C/2.16kg | ISO 1133 | 3.5 g/10min |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/RAMOFIN PPH301G6NT |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 145 °C |
| melting temperature | ISO 11357-3 | 165 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 153 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 153 °C | |
| Continuous use temperature | -- | 100 °C | |
| --2 | 155 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 145 °C |
| melting temperature | ASTM D3417 | 165 °C |