LCP E130i BK205P TAIWAN POLYPLASTICS
LAPEROS®
Household appliances,Household appliances
heat-resisting,Flame retardant,enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 71 |
| thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Hot deformation temperature | 8.0MPa,未退火 | ISO 75-2/C | 216 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 276 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2E-05 cm/cm/°C |
| MD | ISO 11359-2 | 7E-06 cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 335 °C | |
| Vicat softening temperature | ISO 306/B50 | 195 °C |
| mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Bending modulus | 23°C | ISO 178 | 13500 Mpa |
| bending strength | 23°C | ISO 178 | 220 Mpa |
| Compressive modulus | ISO 604 | 14000 Mpa | |
| CompressiveStress | 1%Strain | ISO 604 | 93.0 Mpa |
| Fracture bending strain | ISO 178 | 2.2 % | |
| Tensile modulus | ISO 527-2/1A/1 | 15000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.6 % |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 150 Mpa |
| Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Arc resistance | Internal Method | 140 sec | |
| Compared to the anti leakage trace index | IEC 60112 | V | |
| Dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Dissipation factor | 1MHz | IEC 60250 | 0.025 |
| 2.05GHz | Internal Method | 6E-03 | |
| 100Hz | IEC 60250 | 0.010 | |
| Relative permittivity | 100Hz | IEC 60250 | 4.00 |
| 2.05GHz | Internal Method | 4.23 | |
| 1MHz | IEC 60250 | 3.30 | |
| Surface resistivity | IEC 60093 | 1E+14 ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.10 % |
| TD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.030 % |
| impact performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 43 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 31 kJ/m² |
| flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i BK205P |
|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 45 % | |
| UL flame retardant rating | UL 94 | V-0 |