PC/ABS C7210A-701 SABIC INNOVATIVE US
CYCOLAC™
Electronic field、Electrical field、Thin walled components
High mobility、Flame retardant、Filler: Talc filler
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 5.9E-05 cm/cm/°C |
| RTIElec | UL746 | 90.0 °C | |
| Vicat Softening Temperature | ASTMD15256 | 102 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 92.2 °C |
| RTI | UL746 | 90.0 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 82.2 °C |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 85.0 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.30到0.50 % |
| TD:3.20mm | 0.40到0.60 % | ||
| Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 16 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3140 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 3.6 % |
| 断裂 | 80 % | ||
| Tensile Modulus | 3520 Mpa | ||
| Tensile Strength | 屈服 | 63.4 Mpa | |
| 断裂 | 49.0 Mpa | ||
| Flexural Strength | 断裂,50.0mm跨距 | ASTMD790 | 106 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 47.5 J |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 1900 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Flame Rating | 1.19mm | UL94 | V-0 |
| 1.98mm | 5VB |