Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM CH-20 JAPAN POLYPLASTIC
DURACON®
Automotive sector、Bottle cap、Fiber grade
wear resistant、Carbon fiber reinforced、Conductive、Weather resistance、Thermal stability、Filler: Carbon fiber rein、20% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| ColorNumber | CD3501 |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 95 |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+02 ohms·cm | |
| Surface Resistivity | IEC 60093 | 50 ohms |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 10000 10^-8mm³/N·m |
| Tensile modulus | ISO 527-2 | 14000 Mpa | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.24 |
| Wear factor | 0.49MPa,0.30m/sec4 | JISK7218 | 5.0 10^-8mm³/N·m |
| bending strength | ISO 178 | 205 Mpa | |
| Wear factor | 0.49MPa,0.30m/sec6 | JISK7218 | 300 10^-8mm³/N·m |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ISO 178 | 12000 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.35 |
| Wear factor | 0.060MPa,0.15m/sec5 | JISK7218 | 50 10^-8mm³/N·m |
| tensile strength | ISO 527-2 | 144 Mpa |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.00 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.30 % |
| density | ISO 1183 | 1.47 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.5 g/10min |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.80 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/CH-20 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 8E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 163 °C |