POM KAL-4022 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting、high strength、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 87.0 °C |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 162 °C | |
| 1.8MPa,未退火,3.20mm | 132 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Tensile Elongation | 断裂 | ASTMD638 | 7.4 % |
| Tensile Strain | ISO527-2/5 | 7.4 % | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.23 |
| Tensile Modulus | ISO527-2/1 | 3460 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/5 | 56.0 Mpa |
| Flexural Modulus | ISO178 | 3080 Mpa | |
| 50.0mmSpan | ASTMD790 | 3090 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.16 |
| Tensile Elongation | 屈服 | ASTMD638 | 6.5 % |
| Specific Wear Rate | Ring | ASTMD3702Modified | 0.00 10^-10in^5-min/ft-lb-hr |
| Flexural Stress | ISO178 | 77.0 Mpa | |
| Specific Wear Rate | Washer | ASTMD3702Modified | 8.00 10^-10in^5-min/ft-lb-hr |
| Tensile Modulus | ASTMD638 | 3640 Mpa | |
| Tensile Strength | Break | 58.0 Mpa | |
| Tensile Strain | 屈服 | ISO527-2/5 | 6.3 % |
| Tensile Stress | 57.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Modeling Shrinkage | MD：--2 | 内部方法 | 1.8to2.2 % |
| TD：24hr | ASTMD955 | 2.0to4.0 % | |
| MD：24hr | 2.0to4.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| 23°C | ISO180/1U | 32 kJ/m² | |
| Notched Izod Impact Strength | ISO180/1A | 5.5 kJ/m² |