Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS KF-730 KINGFA LIAONING
KINGFA®
Office equipment application,Electronic and Electrical Applications,Home appliance applications
Universal level,Wide application range
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | KINGFA LIAONING/KF-730 |
|---|---|---|---|
| Load deformation temperature | 0.45MPa | ISO 75-2 | 85 °C |
| 1.8MPa | ISO 75-2 | 77 °C | |
| Vicat softening temperature | 5kg, 50℃/h | ISO 306 | 86 °C |
| 1kg, 120℃/h | ISO 306 | 96 °C |
| mechanical properties | Test Condition | Test Method | KINGFA LIAONING/KF-730 |
|---|---|---|---|
| Bending modulus | 2mm/min | ISO 178 | 2500 Mpa |
| Bending strength | 2mm/min | ISO 178 | 76 Mpa |
| Fracture | 50mm/min | ISO 527-2 | 8 % |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 20 kJ/m² |
| Rockwell hardness | ISO 2039-2 | 108 R scale | |
| tensile strength | 50mm/min | ISO 527-2 | 47 Mpa |
| Electrical performance | Test Condition | Test Method | KINGFA LIAONING/KF-730 |
|---|---|---|---|
| Dielectric strength | IEC 60243-1 | 22 KV/mm | |
| Volume resistivity | IEC 60093 | 100000000000000 ohms·cm |
| Physical properties | Test Condition | Test Method | KINGFA LIAONING/KF-730 |
|---|---|---|---|
| melt mass-flow rate | 220℃, 10kg | ISO 1133-1 | 20 g/10min |
| 200℃, 5kg | ISO 1133-1 | 2 g/10min | |
| Mold shrinkage rate | 23℃ | ISO 2577 | 0.4-0.7 % |