Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA HTV-5H1 EMS-CHEMIE SWITZERLAND
Grivory®
Automotive Applications
Glass fiber reinforced、high strength、High hardness、dimensional stability 、Low warpage、Chemical resistance、Excellent surface finish
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| -30°C | ISO 179/1eU | 80 kJ/m² |
| hardness | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 340 Mpa |
| Mechanical properties | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 18000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| tensile strength | 断裂 | ISO 527-2 | 250 Mpa |
| Electrical performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| Flammability level | UL 94 | HB | |
| ISO Type | ISO 1874 | PA6T/6I. MH. 12-190. GF50 |
| physical property | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.3 % |
| density | ISO 1183 | 1.65 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.10 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 3.0 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.50 % |
| Thermal performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/HTV-5H1 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 325 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 285 °C |
| 8.0 MPa, 未退火，HDT | ISO 75-2/C | 175 °C | |
| Continuous use temperature | --4 | 内部方法 | 250 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 4.0E-5 cm/cm/°C | |
| Continuous use temperature | --3 | ISO 2578 | 150 °C |