HDPE HIPLEX® TR 130 HIP PETROHEMIJA SERBIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 无断裂 |
| Supplementary Information | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| Blow molding temperature | 195to220 °C |
| hardness | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 58 |
| film | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| Elmendorf tear strength | MD:25.0µm | ASTM D1922 | 42.5 kN/m |
| film thickness | 25 µm | ||
| tensile strength | TD:屈服,25µm | ISO 527-3 | 19.0 MPa |
| MD:断裂,25µm | ISO 527-3 | 43.0 MPa | |
| elongation | MD:断裂,25µm | ISO 527-3 | 550 % |
| Dart impact | 25µm | ASTM D1709 | 88 g |
| Elmendorf tear strength | TD:25.0µm | ASTM D1922 | 251.0 kN/m |
| tensile strength | MD:屈服,25µm | ISO 527-3 | 24.0 MPa |
| TD:断裂,25µm | ISO 527-3 | 33.0 MPa | |
| elongation | TD:断裂,25µm | ISO 527-3 | 700 % |
| Mechanical properties | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 32.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 900 % |
| tensile strength | 屈服 | ISO 527-2 | 18.0 MPa |
| physical property | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| Environmental stress cracking resistance | F50 | ASTM D1693B | >1000 hr |
| density | ISO 1183 | 0.940 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.18 g/10min |
| Thermal performance | Test Condition | Test Method | HIP PETROHEMIJA SERBIA/HIPLEX® TR 130 |
|---|---|---|---|
| vicat | ISO 306 | 120 °C |