Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE M80064F SINOPEC FUJIAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SINOPEC FUJIAN/M80064F |
|---|---|---|---|
| 邵氏D,模压成型 | ISO868 | 65 |
| Mechanical properties | Test Condition | Test Method | SINOPEC FUJIAN/M80064F |
|---|---|---|---|
| Tensile stress | 断裂,2.00mm,模压成型 | ISO527-2/1BA/50 | 15.0 Mpa |
| Flexural modulus | 2.00mm,模压成型 | ISO178 | 1700 Mpa |
| Tensile modulus | 2.00mm,模压成型 | ISO527-2/1BA/50 | 1450 Mpa |
| Tensile strain | 断裂,2.00mm,模压成型 | ISO527-2/1BA/50 | >200 % |
| Bending stress | 2.00mm,模压成型 | ISO178 | 32.0 Mpa |
| Tensile stress | 屈服,2.00mm,模压成型 | ISO527-2/1BA/50 | 32.0 Mpa |
| physical property | Test Condition | Test Method | SINOPEC FUJIAN/M80064F |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 8.0 g/10min |
| 190°C/5.0kg | ISO1133 | 22 g/10min | |
| Anti environmental stress cracking 1 | 60°C,3.00mm,Rhodacal-DS10,模压成型 | 内部方法 | 40.0 hr |
| Thermal performance | Test Condition | Test Method | SINOPEC FUJIAN/M80064F |
|---|---|---|---|
| 0.45MPa,未退火 | ISO75-2/B | 95.0 °C | |
| vicat | ISO306/A | 129 °C | |
| ISO11357-3 | 135 °C | ||
| EnthalpyChange | ISO11357-3 | 229 J/g |