Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA66 HTHFE8200 NC010 DUPONT CANADA
Zytel®
Automotive Applications,Home appliance components
Lubricity,Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | DUPONT CANADA/HTHFE8200 NC010 |
---|---|---|---|
Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 138 °C |
1.8MPa,Unannealed | ISO 75-2/A | 126 °C | |
Linear coefficient of thermal expansion | TD:-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C |
MD:-- | ISO 11359-2 | 9E-05 cm/cm/°C | |
MD:-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
TD:-- | ISO 11359-2 | 1E-04 cm/cm/°C | |
Melting temperature | ISO 11357-3 | 300 °C |
mechanical properties | Test Condition | Test Method | DUPONT CANADA/HTHFE8200 NC010 |
---|---|---|---|
Bending modulus | ISO 178 | 2100 Mpa | |
Nominal tensile fracture strain | ISO 527-2 | 14 % | |
Poisson's ratio | ISO 527 | 0.38 | |
Tensile modulus | ISO 527-2 | 2200 Mpa | |
Tensile strain | Yield | ISO 527-2 | 5.5 % |
tensile strength | Yield | ISO 527-2 | 68.0 Mpa |
Electrical performance | Test Condition | Test Method | DUPONT CANADA/HTHFE8200 NC010 |
---|---|---|---|
Surface resistivity | IEC 60093 | -- ohms | |
Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
Physical properties | Test Condition | Test Method | DUPONT CANADA/HTHFE8200 NC010 |
---|---|---|---|
MediumDensity | 0.970 g/cm³ | ||
Shrinkage rate | MD | ISO 294-4 | 0.80 % |
TD | ISO 294-4 | 0.90 % | |
SpecificHeatCapacity of Melt | 2220 J/kg/°C | ||
ThermalConductivityofMelt | 0.18 W/m/K | ||
Top out temperature | 225 °C | ||
Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 1.9 % |
Saturation,23°C,2.00mm | ISO 62 | 6.3 % |
impact performance | Test Condition | Test Method | DUPONT CANADA/HTHFE8200 NC010 |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
23°C | ISO 179/1eU | NoBreak |
flammability | Test Condition | Test Method | DUPONT CANADA/HTHFE8200 NC010 |
---|---|---|---|
Burning rate | 1.00mm | ISO 3795 | <100 mm/min |
FMVSS flammability | FMVSS302 | B | |
UL flame retardant rating | 0.75mm | UL 94 | HB |
0.75mm | IEC 60695-11-10,-20 | HB | |
1.5mm | IEC 60695-11-10,-20 | HB | |
1.5mm | UL 94 | HB |