Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1026 TORAY JAPAN
Amilan®
Automotive sector
Thermal stability、Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Flame Rating | UL 94 | 3.5%水｜- | |
| Melting Temperature | 225 ℃（℉） | ||
| Thermal Conductivity | 3.5%水｜- Kcal/m·hr·℃ | ||
| Specific Heat | 3.5%水｜- Cal/g·℃ | ||
| Coefficient of Linear Thermal Expansion | ASTM D-696 | 3.5%水｜- ×10-5cm/cm/℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | °C | 182 -- |
| Thermal Conductivity | W/m/K | 0.25 -- | |
| Melting Temperature | 差示扫描测热计DSC | 225 °C | |
| Linear thermal expansion coefficient | MD | cm/cm/°C | 8E-05 -- |
| Specific Heat | J/kg/°C | 1900 -- | |
| Deflection Temperature Under Load? | 4.6kg/cm2 | ASTM D-648 | 3.5%水｜- °C |
| Melting temperature | °C | 225 -- |
| Hardness | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Rockwell Hardness | R计秤,80°C | 80 -- | |
| R计秤,23°C | 119 |
| Mechanical Properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Flexural Modulus | 23°C | MPa | 2600 |
| Rockwell Hardness | 80℃ | ASTM D-785 | 3.5%水｜- R-标度 |
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 3.5%水｜520 kg/cm2 |
| Flexural Modulus | 80℃ | ASTM D-790 | 3.5%水｜3000 kg/cm2 |
| Izod Impact Strength | -40℃，无缺口1/2 | ASTM D-256 | 3.5%水｜- kg.cm/cm |
| Tensile Strength(Yield) | 23℃ | ASTM D-638 | 3.5%水｜350 kg/cm2 |
| Tensile Stress | 80°C | MPa | 25.0 20.0 |
| Flexural Stress | 40.0 25.0 | ||
| -40°C | 135 | ||
| Compressive Stress | 23°C | 80.0 -- | |
| Tensile Strength(Yield) | -40℃ | ASTM D-638 | 3.5%水｜1000 kg/cm2 |
| Flexural Modulus | 80°C | MPa | 700 300 |
| Flexural strength | -40℃ | ASTM D-790 | 3.5%水｜1300 kg/cm2 |
| 23℃ | 3.5%水｜400 kg/cm2 | ||
| Tensile Elongation?(Break) | ASTM D-638 | 3.5%水｜<200 % | |
| Tensile Strength | ASTM D-792 | 无水｜720 kg/cm2 | |
| Shearing Strength | 23°C | MPa | 70.0 65.0 |
| Tensile Strength(Yield) | 80℃ | ASTM D-638 | 3.5%水｜200 kg/cm2 |
| Flexural Modulus | 23℃ | ASTM D-790 | 3.5%水｜8000 kg/cm2 |
| -40°C | MPa | 3800 3600 | |
| Tensile Stress | 23°C | 80.0 35.0 | |
| Rockwell Hardness | ASTM D785 | 80 | |
| Tensile Stress | -40°C | MPa | 110 |
| Taber Abrasion Resistance | 1000Cycles | mg | 3.00到4.00 -- |
| Rockwell Hardness | 23℃ | ASTM D-785 | 无水｜119 R-标度 |
| Flexural Stress | 23°C | MPa | 110 40.0 |
| Coefficient of Friction (vs.Metal) | 0.15到0.20 -- | ||
| Tensile Strain | 断裂,23°C | % | 50 |
| Izod Impact Strength | 23℃，无缺口1/8 | 3.5%水｜- kg·cm/cm2 | |
| Compressive Strength | 23℃ | ASTM D-695 | 3.5%水｜650 kg/cm2 |
| Izod Impact Strength | 23℃，无缺口1/8 | ASTM D-256 | 3.5%水｜<50 kg.cm/cm |
| Tensile Strain | 屈服,23°C | % | 1.5 -- |
| Flexural strength | 80℃ | ASTM D-790 | 3.5%水｜250 kg/cm2 |
| Flexural Modulus | -40℃ | 3.5%水｜37000 kg/cm2 |
| Physical | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Modeling Shrinkage | MD：1.00mm3 | % | 0.40到0.90 -- |
| MD：3.00mm4 | 0.80到1.6 -- | ||
| Moisture Absorption | 23°C,24hr | 1.8 -- | |
| Taber wear | 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- mg/1000次 |
| Moisture Absorption | 饱和,23°C | % | 11 -- |
| 23℃，24小时 | ASTM D-570 | 3.5%水｜- % |
| Physical Properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 1.8 % | |
| Density | ASTM D792/ISO 1183 | 1.13 |
| Impact Properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | -40°C | 无断裂 -- | |
| 23°C | 无断裂 -- |
| Flammability | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Flame Rating | HB -- |
| Electrical Properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Volume Resistivity | ohms·cm | 1.0E+13到1.0E+14 1.0E+11到1.0E+12 | |
| ASTM D257/IEC 60093 | 10^11~12 Ω.cm | ||
| ASTM D-257 | 3.5%水｜1011-1012 Ω.cm |