HIPS PH-88 TAIWAN CHIMEI
POLYREX®
Electronic and electrical、Toy accessories、Home Furnishings
heat-resisting
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN CHIMEI/PH-88 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 11 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 98 J/m |
| 23°C,6.40mm | ASTM D256 | 83 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 6.5 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 11 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN CHIMEI/PH-88 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 60 |
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PH-88 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 26.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 40 % |
| bending strength | --5 | ASTM D790 | 37.2 Mpa |
| --6 | ISO 178 | 37.0 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 40 % |
| tensile strength | 断裂4 | ASTM D638 | 23.5 Mpa |
| Flexural modulus | --6 | ISO 178 | 2100 Mpa |
| --5 | ASTM D790 | 1930 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 24.0 Mpa |
| flammability | Test Condition | Test Method | TAIWAN CHIMEI/PH-88 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TAIWAN CHIMEI/PH-88 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.03 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| density | --3 | ASTM D792 | 1.05 g/cm³ |
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 5.50 cm3/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PH-88 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| vicat | -- | ASTM D15257 | 98.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 94.0 °C |
| vicat | -- | ISO 306/A50 | 96.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 89.0 °C |
| vicat | -- | ISO 306/B50 | 90.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 74.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.0E-5到6.0E-5 cm/cm/°C |