Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 450GL15 VICTREX UK
VICTREX®
Non specific food、Medical supplies、Nursing supplies
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 55 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1U | 60 kJ/m² |
| hardness | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 86 |
| Mechanical properties | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| tensile strength | 断裂,275°C | ISO 527-2 | 25.0 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 240 Mpa |
| compression stress | 120°C | ISO 604 | 130 Mpa |
| 200°C | ISO 604 | 40.0 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 7000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 7500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 140 Mpa |
| compression stress | 23°C | ISO 604 | 200 Mpa |
| tensile strength | 断裂,175°C | ISO 527-2 | 45.0 Mpa |
| 断裂,125°C | ISO 527-2 | 80.0 Mpa |
| Electrical performance | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| dielectric constant | 23°C,1kHz | IEC 60250 | 3.10 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 24 KV/mm |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 5E-03 |
| Filling analysis | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| melt viscosity | 400°C | ISO 11443 | 450 Pa·s |
| physical property | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| spiral flow length | 内部方法 | 10.0 CM | |
| density | 比重 | ISO 1183 | 1.38 g/cm³ |
| Water absorption rate | 23°C,24hr,3.20mm | ISO 62 | 0.060 % |
| Shrinkage rate | TD:180°C | ISO 294-4 | 0.90 % |
| MD:180°C | ISO 294-4 | 0.50 % | |
| Water absorption rate | 平衡,23°C,3.20mm,50%RH | ISO 62 | 0.40 % |
| Thermal performance | Test Condition | Test Method | VICTREX UK/450GL15 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD:>143°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| thermal conductivity | 23°C | ISO 22007-4 | 0.30 W/m/K |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 298 °C |
| melting temperature | ISO 11357-3 | 343 °C | |
| Linear coefficient of thermal expansion | MD:<143°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| specific heat | 23°C | DSC | 1700 J/kg/°C |
| Linear coefficient of thermal expansion | TD:>143°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| TD:<143°C | ISO 11359-2 | 5E-05 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 143 °C |