Polyester, TP Mar-Bal MB2000-10 Mar-Bal, Inc.
--
--
Filler, glass fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 210to320 J/m |
| hardness | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| Barcol Hardness | ASTM D2583 | 35to45 |
| Electrical performance | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| Inclined plate electric trace | ASTM D2303 | >1000 min | |
| dielectric strength | ASTM D149 | >13 kV/mm | |
| arc resistance | ASTM D495 | >185 sec |
| Mechanical properties | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| tensile strength | ASTM D638 | 31.0to37.9 MPa | |
| compressive strength | ASTM D695 | 117to131 MPa | |
| Flexural modulus | ASTM D790 | 8960to11000 MPa | |
| Compression Modulus | ASTM D695 | 359000to379000 MPa | |
| bending strength | ASTM D790 | 89.6to110 MPa | |
| shear strength | ASTM D732 | 41.4to48.3 MPa |
| flammability | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.050to0.30 % |
| ASTM D1895 | 1.0 | ||
| Water absorption rate | 24hr | ASTM D570 | 0.14 % |
| density | ASTM D792 | 1.80to1.90 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mar-Bal, Inc./Mar-Bal MB2000-10 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | >260 °C |