Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM NW-02C TAIWAN POLYPLASTICS
DURACON® 
Electrical field、Electronic field、Fitness equipment、Automotive sector、Bottle cap
High sliding、wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Supplementary InformationTest ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
ColorNumberCF2001/CD3501
hardnessTest ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
Rockwell hardnessM级ISO2039-270
Electrical performanceTest ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
Surface ResistivityIEC600933E+15 ohms
Volume resistivityIEC600931E+14 ohms·cm
dielectric strength3.00mmIEC60243-120 KV/mm
Mechanical propertiesTest ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
Nominal tensile fracture strainISO527-220 %
Wear factor0.98MPa,0.30m/sec4JISK7218<1.0 10^-8mm³/N·m
0.060MPa,0.15m/sec7JISK72181000 10^-8mm³/N·m
0.98MPa,0.30m/sec5JISK721819 10^-8mm³/N·m
0.060MPa,0.15m/sec6JISK7218300 10^-8mm³/N·m
与钢-动态3JISK72180.17
Tensile stressISO527-252.0 Mpa
Dynamic2JISK72180.37
Bending stressISO17872.0 Mpa
Tensile modulusISO527-22350 Mpa
Flexural modulusISO1782200 Mpa
flammabilityTest ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
UL flame retardant ratingUL94HB
physical property Test ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
Shrinkage rateMD:2.00mmISO294-42.0 %
melt mass-flow rate190°C/2.16kgISO113320 g/10min
Shrinkage rateTD:2.00mmISO294-41.8 %
Melt volume flow rate190°C/2.16kgISO113318.0 cm3/10min
Water absorption rate23°C,24hrISO620.70 %
Thermal performanceTest ConditionTest MethodTAIWAN POLYPLASTICS/NW-02C
1.8MPa,未退火ISO75-2/A85.0 °C
MD：23到55°C内部方法1.2E-04 cm/cm/°C
TD：23to55°C内部方法1.2E-04 cm/cm/°C