LLDPE LL7410D1 PTT THAI
InnoPlus
Thermoforming Applications,Lining,Agricultural applications,film,Food packaging
low density,Anti perforation,High toughness,high strength,Low smoothness,Low resistance to agglome
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | PTT THAI/LL7410D1 |
|---|---|---|---|
| tensile strength | MD : 断裂, 25 µm, 吹塑薄膜 | ASTM D882 | 34.0 Mpa |
| elongation | MD : 断裂, 25 µm, 吹塑薄膜 | ASTM D882 | 600 % |
| Dart impact | 25 µm, 吹塑薄膜 | ASTM D1709 | 90 g |
| Secant modulus | 1% 正割, TD : 25 µm, 吹塑薄膜 | ASTM D882 | 230 Mpa |
| 1% 正割, MD : 25 µm, 吹塑薄膜 | ASTM D882 | 190 Mpa | |
| Elmendorf tear strength | MD : 25 µm, 吹塑薄膜 | ASTM D1922 | 100 g |
| Film thickness - tested | 25 µm | ||
| elongation | TD : 断裂, 25 µm, 吹塑薄膜 | ASTM D882 | 800 % |
| tensile strength | TD : 断裂, 25 µm, 吹塑薄膜 | ASTM D882 | 26.0 Mpa |
| Elmendorf tear strength | TD : 25 µm, 吹塑薄膜 | ASTM D1922 | 300 g |
| optical performance | Test Condition | Test Method | PTT THAI/LL7410D1 |
|---|---|---|---|
| gloss | 45°, 25.0 µm, 吹塑薄膜 | ASTM D2457 | 50 |
| Haze ratio | 25.0 µm, 吹塑薄膜 | ASTM D1003 | 13 % |
| squeeze out | Test Condition | Test Method | PTT THAI/LL7410D1 |
|---|---|---|---|
| Melt Temperature | 160 to 180 °C | ||
| die temperature | 170 to 190 °C |
| physical property | Test Condition | Test Method | PTT THAI/LL7410D1 |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16 kg | ASTM D1238 | 1.0 g/10 min |
| Thermal performance | Test Condition | Test Method | PTT THAI/LL7410D1 |
|---|---|---|---|
| vicat | ASTM D1525 | 101 °C | |
| melting temperature | ASTM D3418 | 121 °C |