AS(SAN) 378PG7 BASF GERMANY
Luran®
Automotive components
heat-resisting、enhance、35%GF
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | BASF GERMANY/378PG7 |
|---|---|---|---|
| Oxygen Index | 20 % |
| Basic performance | Test Condition | Test Method | BASF GERMANY/378PG7 |
|---|---|---|---|
| Water absorption rate | 0.25 % | ||
| density | 1360 kg/m | ||
| melt mass-flow rate | 220℃/10kg | 5 CM |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/378PG7 |
|---|---|---|---|
| dielectric constant | 1MHz | 3.2 | |
| Dissipation factor | 100Hz | 70 E-4 | |
| Volume resistivity | >1E13 Ω.m | ||
| Surface Resistivity | >1E15 Ω | ||
| dielectric strength | 39 KV/mm | ||
| Relative Arc Track Mathematical CTI | 600 | ||
| dielectric constant | 100Hz | 3.5 | |
| Dissipation factor | 1MHz | 100 E-4 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/378PG7 |
|---|---|---|---|
| Charpy impact strength | 23℃ | 17 KJ/m | |
| -30℃ | 17 KJ/m | ||
| Charpy notch impact strength | 23℃ | 4 KJ/m | |
| Tensile elongation modulus | 1h | 9500 Mpa | |
| tensile breaking strength | 110 Mpa | ||
| Tensile modulus | 12000 Mpa | ||
| Tensile elongation modulus | 1000h | 7500 Mpa | |
| Tensile fracture elongation | 2 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/378PG7 |
|---|---|---|---|
| Linear expansion coefficient | 平行方向 | 0.25 E-4/℃ | |
| Heat Deflection Temperature | 1.80MPa | 105 °C | |
| 0.45MPa | 108 °C | ||
| vicat | 50℃/H50n | 109 °C | |
| Flammability | 1.6mm | UL 94 | HB |