PA66 G3000HR INVISTA USA

TORZEN®

Automotive sector、Electronic field、Electrical field

Hydrolysis resistance、Dimensional stability、Glass fiber reinforced、Thermal stability、Filler: Glass fiber reinf、Good dimensional stabilit、High tensile strength、Hydrolysis resistance、thermal stability、Good demolding performanc、30% filler by weight

Plastic Datasheets

Mechanical properties	Test Condition	Test Method	INVISTA USA/G3000HR
Charpy Notched Impact Strength	-40℃	ISO 179	9.0 kJ/m²
Tensile modulus		ISO 527-2	9800 Mpa
tensile strength	断裂	ISO 527	195 Mpa
bending strength		ISO 178	270 Mpa
Flexural modulus		ISO 178	9100 Mpa
Tensile strain	断裂	ISO 527-2	3.1 %
tensile strength	断裂	ISO 527-2	195 Mpa
elongation at break		ISO 527	3.1 %
Charpy Notched Impact Strength	23℃	ISO 179	10 kJ/m²
Tensile modulus		ISO 527	9800 Mpa
Impact strength of cantilever beam gap	23℃	ISO 180	10 kJ/m²

physical property	Test Condition	Test Method	INVISTA USA/G3000HR
Shrinkage rate	MD: 2.00 mm	ISO 294-4	0.30-0.40 %
Shrinkage rate		MD:2.00mm	ISO 294-4	0.30-0.40 %
Water absorption rate	23°C,24hr	ISO 62	1.2 %
Shrinkage rate	TD: 2.00 mm	ISO 294-4	0.95-1.05 %
Water absorption rate	23℃, 24 hr	ISO 62	1.2 %
Water absorption rate		平衡,23°C,50%RH	ISO 62	1.8 %
Shrinkage rate	TD:2.00mm	ISO 294-4	0.95-1.1 %
Water absorption rate	平衡, 23℃, 50% RH	ISO 62	1.8 %

Thermal performance	Test Condition	Test Method	INVISTA USA/G3000HR
melting temperature		ISO 11357-3	262 °C
Heat distortion temperature	0.45 MPa, 未退火，HDT	ISO 75	255 °C
melting temperature	10 ℃/min	ISO 11357	262 °C
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	255 °C
		1.8MPa,未退火，HDT	ISO 75-2/A	248 °C
		1.82 MPa, 未退火，HDT	ISO 75	248 °C