PA66 70G30HSLR BK099 DUPONT SHENZHEN
Zytel® 
Electrical field、Electronic field、Fitness equipment、Automotive sector、Electrical appliances
Thermal stability、Lubricity、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
Impact strength of simply supported beam without notch23°CISO 179/1eU80 kJ/m²
-30°CISO 179/1eU60 kJ/m²
Mechanical propertiesTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
Tensile modulusISO 527-29800 Mpa
Tensile stress断裂ISO 527-2195 Mpa
Tensile strain断裂ISO 527-23.5 %
Electrical performanceTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
Compared to the Leakage Tracking Index (CTI)3.00 mmUL 746PLC 0
CTIIEC 60112600 V
Dissipation Factor100 HzIEC 62631-2-10.016
1 MHzIEC 62631-2-10.016
Volume resistivityIEC 62631-3-11.0E+11 ohms·m
Surface ResistivityIEC 62631-3-2-- ohms
flammabilityTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
FMVSS flammabilityFMVSS 302SE/B
atomizationF-value (refraction)ISO 645295 %
UL flame retardant rating0.71 mmUL 94, IEC 60695-11-10, -20HB
1.5 mmUL 94, IEC 60695-11-10, -20HB
Limiting Oxygen IndexISO 4589-224 %
atomizationG-value (condensate)ISO 64523.0E-4 g
burning rate1.00 mmISO 379524 mm/min
Filling analysisTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
OdorVDA 2704.50
Melt density1.21 g/cm³
Specific Heat Capacity of Melt2290 J/kg/°C
Thermal Conductivity of Melt0.21 W/m/K
Emission of Organic CompoundsVDA 2776.00 µgC/g
physical property Test ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
Water absorption rate饱和, 23°C, 2.00 mmISO 626.9 %
平衡, 23°C, 2.00 mm, 50% RHISO 622.0 %
Shrinkage rate流量ISO 294-40.30 %
横向流量ISO 294-41.1 %
Thermal performanceTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
0.45 MPa, 未退火ISO 75-2/B260 °C
流动ISO 11359-22.8E-5 cm/cm/°C
横向ISO 11359-29.5E-5 cm/cm/°C
Glass transition temperature 3ISO 11357-280.0 °C
Melting temperature 3ISO 11357-3262 °C
1.8 MPa, 未退火ISO 75-2/A253 °C
Effective Thermal Diffusivity6.85E-8 m²/s
injectionTest ConditionTest MethodDUPONT SHENZHEN/70G30HSLR BK099
Maximum Screw Tangential Speed12 m/min
Temperature70 到 120 °C
Drying time - hot air dryer2.0 到 4.0 hr
Melt Temperature, Optimum295 °C
Processing (melt) temperature285 到 305 °C
Hold Pressure Time3.00 s/mm
drying temperature80 °C
Mold Temperature, Optimum100 °C
pressure holding50.0 到 100 Mpa
Suggested maximum moisture content0.20 %
pressure holdingDrying Recommendedyes