Certificates
PC XHT2143 NA7D006T SABIC INNOVATIVE US
LEXAN™
Lighting applications,Automotive External Parts,Architectural Applications
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XHT2143 NA7D006T |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 68.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XHT2143 NA7D006T |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2600 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 70.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 90 % |
| 断裂 | ISO 527-2/50 | 90 % | |
| Flexural modulus | --5 | ISO 178 | 2450 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 110 Mpa |
| --5,6 | ISO 178 | 100 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2550 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| 屈服 | ISO 527-2/50 | 70.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 6.5 % |
| 屈服3 | ASTM D638 | 6.5 % | |
| tensile strength | 断裂3 | ASTM D638 | 60.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2600 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XHT2143 NA7D006T |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.23 % |
| melt mass-flow rate | 330°C/2.16 kg | ASTM D1238 | 46 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| Melt volume flow rate | 330°C/2.16 kg | ISO 1133 | 43.0 cm3/10min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.60 - 0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XHT2143 NA7D006T |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 6.0E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 162 °C |
| -- | ASTM D15259 | 161 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 6.0E-5 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 160 °C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 155 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 142 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 6.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 145 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/XHT2143 NA7D006T |
|---|---|---|---|
| screw speed | 40 to 90 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 290 to 330 °C | ||
| drying temperature | 135 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 280 to 320 °C | ||
| Temperature at the rear of the barrel | 270 to 310 °C | ||
| Exhaust hole depth | 0.025 to 0.080 mm | ||
| Temperature at the front of the material cylinder | 290 to 330 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 85 to 130 °C | ||
| Spray nozzle temperature | 285 to 325 °C |