PC/ABS MB2213R MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and Electrical
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 130 °C |
| 1.8MPa,未退火 | ISO75-2/A | 110 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2400 Mpa | |
| Tensile Strain | 屈服 | ISO527-2 | 4.9 % |
| Tensile Stress | 屈服 | ISO527-2 | 59.0 Mpa |
| Nominal Tensile Strain at Break | ISO527-2 | 76 % | |
| Flexural Stress | ISO178 | 94.0 Mpa | |
| Tensile Modulus | ISO527-2 | 2500 Mpa |
| Physical | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Modeling Shrinkage | 吸水率(饱和,23°C) | 0.12 % | |
| Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 9.00 cm3/10min |
| Modeling Shrinkage | TD:3.20mm | 0.40to0.60 % | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 9.0 g/10min |
| Modeling Shrinkage | MD:3.20mm | 0.40to0.60 % |
| Impact Properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak |
| Flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Flame Rating | 1.0mm | UL94 | HB |