Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA A-1133HS BK324 SOLVAY USA
AMODEL®
--
Filler: Glass fiber reinf、33% filler by weight、Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/A-1133HS BK324 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 319 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.8 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 11600 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 13400 Mpa |
| elongation at break | 23°C | ISO 527-2 | 2.5 % |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 49 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 73 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 233 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/A-1133HS BK324 |
|---|---|---|---|
| dielectric strength | 3.20mm | IEC 60243-1 | 39 KV/mm |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | SOLVAY USA/A-1133HS BK324 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.5mm | |
| UL -94 | HB 3.0mm | ||
| UL -94 | HB 0.84mm |
| physical property | Test Condition | Test Method | SOLVAY USA/A-1133HS BK324 |
|---|---|---|---|
| density | ISO 1183 | 1.48 g/cm³ |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/A-1133HS BK324 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 280 °C |
| vicat | 熔融温度 | ISO 11357-3 | 313 °C |