Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GN-3610L TEIJIN JAPAN
PANLITE®
machine、Mechanical components
High rigidity、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 4E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 80.0 °C |
| RTIElec | 80.0 °C | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 143 °C |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 146 ℃（℉） | |
| RTIStr | 1.5mm | UL746 | 80.0 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 140 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 6E-05 cm/cm/°C |
| Vicat Softening Temperature | ISO306/B50 | 146 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000060 mm/mm.℃ | |
| Heat Deflection Temperature | ASTM D648/ISO 75 | 143 ℃（℉） |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.40to0.60 % |
| MD:4.00mm | 0.30to0.50 % | ||
| Moisture Absorption | 23°C,24hr | ISO62 | 0.16 % |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Flexural Modulus | ISO178 | 3600 Mpa | |
| Flexural Strength | ASTM D790/ISO 178 | 115 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 2.0 % | |
| Tensile Strength | 70.0 kg/cm²(MPa)[Lb/in²] | ||
| Tensile Strain | 断裂 | ISO527-2/5 | 2.0 % |
| Tensile Modulus | ISO527-2/1 | 3800 Mpa | |
| Flexural Stress | ISO178 | 115 Mpa | |
| Tensile Modulus | ASTM D638/ISO 527 | 3800 kg/cm²(MPa)[Lb/in²] | |
| Tensile Stress | 断裂 | ISO527-2/5 | 70.0 Mpa |
| Flexural Modulus | ASTM D790/ISO 178 | 3600 kg/cm²(MPa)[Lb/in²] |
| Other | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Remarks | 以上加工数据，为参考值.以生产厂商设备的实际状况而进行调整。 |
| Impact Properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | 45 kJ/m² |
| Physical Properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.16 % | |
| Modeling Shrinkage | ASTM D955 | 0.40-0.60 % |
| Flammability | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Flame Rating | 1.0mm4 | UL94 | V-1 |
| 0.40mm | V-2 | ||
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| 3.0mm | 850 °C | ||
| Flame Rating | 1.6mm | UL94 | V-0 |
| Glow Wire Flammability Index | IEC60695-2-12 | 960 °C | |
| 3.0mm | 960 °C | ||
| 1.0mm | 960 °C | ||
| Glow Wire Ignition Temperature | 1.6mm | IEC60695-2-13 | 850 °C |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 35 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Constant | 100Hz | IEC60250 | 3.20 |
| Comparative Tracking Index | IEC60112 | 175 V | |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω | |
| Dielectric Constant | ASTM D150/IEC 60250 | 3.20 | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω.cm | |
| Dissipation Factor? | 1MHz | IEC60250 | 9E-03 |
| Dielectric loss | ASTM D150/IEC 60250 | 0.0090 | |
| Dielectric Constant | 1MHz | IEC60250 | 3.20 |
| Dissipation Factor? | 100Hz | 1E-03 |